Silicone Primer CL-24CW HTV Silicone To Aluminium CL-24CW, Silicone primer of high temperature curing type, is to bond peroxide-cure silicone rubber with substrates like metallics (Metal, Carb
|Tel: +0086-180 9899 4276|
CL-24CW, Silicone primer of high temperature curing type, is to bond peroxide-cure silicone rubber with substrates like metallics (Metal, Carbon steel, Stainless Steel, Aluminum, aluminium alloy).
Good Adhesion Strength
The Silicone is broken when is torn from Aluminium
Adhesion strength reached over 2Mpa
silicone product ok rate reached 99%
No partial bonding failure
Exclusive Patents , General Use
Labour Cost- Saving
Easy processing, Can be dipped , No corrosion To Aluminium
The Silicone primer Can be dried in room temperature , Can be baked to dry
3 Times Standard Tests before goods release
No adhesion failure.
Appearance : Red liquid
Adhesion Strength : ≥2MPa
Specifical gravity : 0.79g/cm³
Temperature tolerance : -60~180℃
Break down voltage : 30KV/cm2
1, Treat the substrates with blast sanding, polishing or wash with industrial alcohol.
2, Brushing, painting, dipping or spraying the CL-24CW on the substrates.
3, Leave dry in room temp for 30 minutes or baking at 110-130℃ for 5-15mintes.
4, The primer treated substrates are processed within that day.
5, The first cure is suitable to DBPH system silicone rubber and the second cure the temperature maximum at 200℃
1, Please cap its cover immediately after use to avoid volatilization.
2, Store the used and unused adhesive in separate way to lengthen the shelf life.
3, After the primer coated on the substrates, leave it volatilize completely before entering the mold, otherwise, there will be bubbles in the finished products.
4, Wash clean the substrates to remove dirts or oil to avoid bad adhesion.
5, Flush with water quickly once contacting with eyes accidently during use.