CL-24S-2, Silicone primer, is to bond peroxide-cure HTV silicone with galvanised metal (carbon steel, stainless steel, metal ).
Appearance : Shallow yellow transparent liquids
|Adhesion Strength : ≥2MPa|
|Specifical gravity : 0.79g/cm3|
Good Adhesion Strength
The Silicone is broken when is torn from Galvanised metal
Adhesion strength reached over 2Mpa
Silicone Product Ok rate reached 99 %
No partial bonding failure
Exclusive Patents , General Use
Labour Cost- Saving
Easy processing, Can be dipped , No corrosion To Galvanised metal
The Silicone primer Can be dried in room temperature , Can be baked to dry
3 Times Standard Tests before goods release
No adhesion failure.
1, Treat the substrates with blast sanding, polishing or wash with industrial alcohol.
2, Brushing, painting, dipping or spraying the CL-24S-2 on the substrates.
3, Leave dry in room temp for 30 minutes or baking at 110-130℃ for 5-15 minutes.
4, The primer treated substrates are processed within that day.
5, The first cure is suitable to DBPH system silicone rubber and the second cure the temperature maximum at 200℃.
1, Please cap its cover immediately after use to avoid volatilization.
2, Store the used and unused adhesive in separate way to lengthen the shelf life.
3, After the primer coated on the substrates, leave it volatilize completely before entering the mold, otherwise, there will be bubbles in the finished products.
4, Wash clean the substrates to remove dirts or oil to avoid bad adhesion.
5, Flush with water quickly once contacting with eyes accidently during use.