Phone screen PET protective film adhesive
Phone screen PET protective film adhesive

Phone Screen Protective Film Adhesive KL-2610B       KL-2610B is a heat and fast cured type of Liquid addition silicone adhesives, it matched with platinum catalysts P4000, tackfier KL-298 and KL-6600 in use, spared from the

Product Specification:
Model No. : KL-2610B
Minimum Order Quantity :   
Lead Time:7-10 Days
Payment Terms:   T/T, Western Union, Paypal
Package:   1
Tel: +0086 -180 9899 4276
Fax: +86 755 8147 8872
E-mail: sales@bondsil.com

Phone Screen Protective Film Adhesive KL-2610B

Applications-7e54f

KL-2610B is a heat and fast cured type of Liquid addition silicone adhesives, it matched with platinum catalysts P4000, tackfier KL-298 and KL-6600 in use, spared from the use of base coating agent, good flowing capability before cured ,The cured silicone adhesive has a good adhesion to stick with PET base material and improve the surface Stripping Resistance. After cured,the adhesives had excellent adhesion, high grade of transparency, good air dispersing capacity , no adhesive residue, high temperature and high humidity resistance, can directly replace the same level products of Dow Corning and KCC products.

Mainly applied to the computer display screen, mobile phone screen protector, PET touch screen film series.Can be coated to PET film by lamination machine.

PSA adhesive for PET filmProductAdvantage-3811e

Reusable for PET film

The PET Film can peel off

frequently from the protective surface.

Metal bonding silicone, plastic bonding silicone, organic silicone adhesive, electronic adhesive, high transparent silicone, leather liquid silicone, self-adhesive silicone, silicone pressure-sensitive adhesive, silicone for optical film, silane coupling agent, platinum vulcanizer,

 

Customised peeling (force) adhesion

Adjustable peeling strength at 0~ 1200g , spare from primering base

Precise concoction of peeling adhesion

Low peeling adhesion easy peel , high absorbing properties

Customised Peel adhesion PSA Silicone Adhesive

Zero silicone transfer

No adhesive residue ,Zero silicone transfer in full weather

No adhesive remains

Metal bonding silicone, plastic bonding silicone, organic silicone adhesive, electronic adhesive, high transparent silicone, leather liquid silicone, self-adhesive silicone, silicone pressure-sensitive adhesive, silicone for optical film, silane coupling agent, platinum vulcanizer,

Double 85 tests

Peel adhesion don't grow heavier in high temperature & High humidity condition

Products quality more stable ,easy rework , no adhesive remains ,weather resistance

The supplier for Apple , Huawei

Metal bonding silicone, plastic bonding silicone, organic silicone adhesive, electronic adhesive, high transparent silicone, leather liquid silicone, self-adhesive silicone, silicone pressure-sensitive adhesive, silicone for optical film, silane coupling agent, platinum vulcanizer,

 

ProductSpecifications-63e41

Appearance And Component:

2610B: Transparent silica gel

P4000:Platinum catalysts

KL-298: Tackifier(Increase the adhesion between silicone adhesive with PET)

KL-6600: High adhesion PSA silicone adhesives(Increase the surface stripping resistace /Peel adhesion)

Viscosity: <35000mpa.s

Solid Content: 60%

Curing Condition: TC10:19S*150℃

TC90:42S*150℃

Stored Condition: Room temperature

Light Transmittance: 94%

Refractive index (sodium yellow light wavelength 5893 10 ^ - 10 meters) : 1.48

Storage:Stored at room temperature for 6 months without mixing.

 

Processing-1bde4

(For example, coated 10 microns stripping force 3g/25 mm)

1.Dented roller coating method:Solid content 24% ,mixing in uniformity with solvent by a weight ratio of P4000:2610B:KL-298:6600:Solvent =1:200:10:40:340

Comma Knife coating method:Solid content 35% ,mixing in uniformity with solvent by a weight ratio of P4000:2610B:KL-298:6600:Solvent=1:200:10:40:160

2. Taking material according to proportion, firstly mix KL-298 with solvent evenly ,orderly followed by 6600→2610B→P4000, thoroughly mixture for 20 minutes

3. Defoaming treatment with vacuum by requirements. Coating uniformity of silicone adhesive on the silicone or PET film surface by coating method.

4. Curing : (Example:coating thickness: 10μm) baking for 1 minutes at 130℃.

Production coating method for reference

Set the oven temperature as from 90 ℃ to 160 ℃ to 140 ℃, The baking time and temperature is adjusted according to the coating quantity,the adhesive thickness of the coating when 10μm, glue baking time control between 50 to 60 seconds ,the adhesive thickness of the coating when 20 microns,glue baking time should be controlled in 100 ~ 120 seconds is advisable.Please change according to the specific equipment and operation method.

Attention-7f20a

1,The solvent is better to choose mixed solvent,Such as xylene:acetic ether:cyclohexanone=80:15:5 or toluene:butanone=1:1

2,The application ratio should be adjusted appropriate to different materials, the thickness of coating and weather conditions (temperature and humidness). The application ratio should be increase platinum catalysts 5%~10% based raw ratio at hot and humid conditions.

3, KL - 298 is volatile,for a long time place will thicken,in use process need to adjust the adding proportion according to the proportion of volatile,otherwise the stripping force will increase .

4,The base material surface by adhesive through corona treatment,Cleaning base materials and keep it dry, no dust and oil.

5,Controlling and checking the viscosity during the coating process. Pay attention to have enough quantity for once and make it deeply cured.

6,Keep in a good and suitable condition for coating. The working shop should be dust-free at 25~35℃ and humidity controlled in 15 ~ 60%.Too much dust will cause adverse, Low over temperature will cause poor flow flat and adhesion strength decline , Large over humidity will cause shrinkage cavity of film. Low over humidity of the electrostatic potential safety hazard,appear on the surface of white and moire phenomenon.

7,The mixed silicone adhesive should be used up within 6 hours, if high viscosity happens,should stop using.

8,The adhesive after mixture containing volatile solvent,the work place should be ventilated and workers should wear labor protection tools during the coating process. Away from flame, high temperature and pay attention to static electricity.

9,Please read the product safety instructions before use.

OURADVANTAGE-310d5Metal bonding silicone, plastic bonding silicone, organic silicone adhesive, electronic adhesive, high transparent silicone, leather liquid silicone, self-adhesive silicone, silicone pressure-sensitive adhesive, silicone for optical film, silane coupling agent, platinum vulcanizer,

 

 

 

 

Sorry,Here is the product description, there is no data!
Sorry,Here is the product notes, there is no data!
May you like

contact us

Mobile:

+0086 -180 9899 4276 Gary Lee

+0086 -135 0281 9396 Wendy Wei

+0086 -138 2374 7978 Kyler Yang

Fax:

+86 755 8147 8872

Address:

H Building ,Xinwei The 3rd Industrial Park,Dalang Street,Longhua New District , Shenzhen City ,Guangdong Province ,China

Message

Technical support:lamp-magic