Base Coating Agent CL-26AB-8 - PET Protective Film Adhesive
Base Coating Agent CL-26AB-8 - PET Protective Film Adhesive
Base Coating Agent CL-26AB-8

Product Specification:
Model No. : CL-26AB-8
Minimum Order Quantity :   2KG
Lead Time:5-7 days
Payment Terms:   T/T, Western Union, Paypal
Package:   1KG/bottle
Tel: +0086-138 -2374 -7978
Fax: 0086-755-81478372
E-mail: export@klbsilicone.com

Base Coating Agent CL-26AB-8


Applications


Mainly apply as base coating agent on the nylon(PA), polyimide(PI)  PET(polyethylene terephthalate), epoxy resin, Bakelite, organic glass etc  later join with unvulcanized platinum -addition silicone rubber in the curing process which result in tight bond between substrates with silicone rubber .it also applied as OCA Lamination glue for OCA protective film or high temperature tapes when matched with KL-2610/KL-6600 or K7657 in use.



Product Specifications


1, They can be glued well for many kinds of mixed silicone and rubber, including once vulcanization and second vulcanization

of silicone material, BPO vulcanized PSA raw silicone

2, Double component, single coating, simple process.

3, Water resistance, anti-salt mist, chemicals resistance, anti-oils, solvent and resisting for severe rugged environment


Performance

AppearanceTransparent pasty form   

ComponentA: Pasty fluid  B: Platinum catalyst

RatioA:B=1:1

SolventComponent solvent                  

Packing:1KG/barrel.

Shelf lifeThree months (25℃) without cover opened.



Processing


1, Surface Treatment: The surface should be cleaned or degreased by chemical cleaning agent or Corona Treatment

2, Coating Method: Firstly, thoroughly mixed A and B, and then painting, dipping, spraying or printing on the substrates

3, Drying condition: Baking at 120°C for 3 minutes.(Baking temperature and time can be adjusted based on thickness of substrates)

4, Temporary Storage: All the products which coated should be use within 24 hours, and  place away from pollution and high temperature or humidity, mixed adhesive should be used up within 3 days.

5, Bonding Method: Silicone raw material gluing with other material should be molded at high temperature or processed with hot air vulcanization.



Attention


1, Storage at a cool place and far away from heat and open flame.

2, Solvent is volatile, please cover the container tightly when done using it

3, The workplace should be ventilated and avoided fire. Prevent breathing or contacting with the skin for a long time.